Fabric care compositions

ABSTRACT

Polyurethaneurea compositions in the form of powders and dispersions are provided for enhancing properties of washed fabric including easy care, better iron gliding, improved shape retention, perfume substantiation and stain management properties.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims the benefit of U.S. Provisional Application No.60/837,011 filed on Aug. 11, 2006 and claims the benefit U.S.Provisional Application No. 60/865,091 filed on Nov. 9, 2006 and is acontinuation-in-part of U.S. application Ser. No. 11/351,967 filed onFeb. 10, 2006 which is a continuation-in-part of U.S. application Ser.No. 11/300,229 filed on Dec. 13, 2005, which is a continuation-in-partof U.S. application Ser. No. 11/253,927 filed on Oct. 19, 2005, which isa continuation in part of U.S. application Ser. No. 11/056,067 filed onFeb. 11, 2005, now U.S. Pat. No. 7,240,371, and is also acontinuation-in-part of Ser. No. 11/654,753 filed on Jan. 18, 2007,which claims the benefit of U.S. application Ser. No. 60/759,853 filedon Jan. 18, 2006, all of which are incorporated herein by reference.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention includes polyurethaneurea compositions havingfabric care properties. Fabric care compositions including detergentsand fabric softeners which include the polyurethaneurea compositions arealso provided.

2. Summary of Related Art

Fabric softeners are often used in addition to detergents to impartsoftness and/or fluffiness to washable fabrics. Fabric softeners alsomake fabrics feel smooth, decrease static cling, impart a pleasingfragrance, reduce drying time, reduce wrinkling and make ironing easier.However, the benefits of these properties generally decrease over timeafter washing.

The most common active components are based on long chain fatty typemolecules called quaternary ammonium compounds, which are cationic innature. Therefore, in order to prevent undesired reaction withdetergents which may be anionic in nature, fabric softeners aregenerally introduced during fabric rinsing or drying.

In order to reduce the time and expense of fabric laundering, there is aneed for fabric care compositions which may be added simultaneously withthe detergent. There is also a need for fabric care compositions whichextend the duration of the benefits of fragrance substantiation and easeof care associated with fabric softening compositions.

SUMMARY OF THE INVENTION

The present invention provides a polyurethaneurea in the form of apowder or an aqueous dispersion that provides fabric care propertieseither alone or in combination with a detergent or fabric softenercomposition.

In one embodiment, a fabric care composition is in the form of non-ionicor anionic film forming dispersion including a polyurethaneurea polymerand water. The polymer is the reaction product of a prepolymer withwater as a chain extender where the prepolymer is the reaction productof a glycol or a mixture of glycols and a polyisocyanate such as4,4′-methylenebis(phenyl isocyanate).

In another embodiment, a fabric care composition is in the form of anionic film forming dispersion including a polyurethaneurea polymer andwater. The ionic nature of the dispersion may be the result of thecombination of a non-ionic polymer dispersion with cationic or anionicsurfactants or additives. Alternatively, where the dispersion isanionic, this may result from the inclusion of ionic groups in thepolyurethaneurea polymer.

In another embodiment is a nonionic non-film-forming dispersionincluding water and a polyurethaneurea polymer. The polymer is thereaction product of a prepolymer and a chain extender such as a diaminechain extender, water and combinations thereof, where the polymer is thereaction product of a glycol (polyol) or a mixture of glycols and apolyisocyanate such as 4,4′-methylenebis(phenyl isocyanate). The polymermay then be filtered and ground or spray dried to provide a powder.

A further embodiment provides a method of extending perfume or fragrancesubstantiation on a fabric or garment. The method includes contactingthe fabric or garment with a fragrance and a polyurethane ureacomposition in the form of a powder or an aqueous dispersion. Thecontact may occur in a variety of ways including, but not limited to,adding the fragrance and polyurethaneurea to a detergent or fabricsoftener prior to laundering and/or drying the fabric, adding themdirectly to the wash water, or introducing them during the rinsingcycle, either directly or in combination with a fabric softenercomposition.

A further embodiment provides a method of providing desired propertiesto a fabric or garment. The method includes contacting a fabric with apolyurethaneurea in the form of a powder or an aqueous dispersion. Thedesired properties which may be imparted to the fabric include, but arenot limited to, shape retention, shape recovery, ease of care (i.e.,ease of ironing, anti-wrinkle), and anti-stain properties.

DETAILED DESCRIPTION OF THE INVENTION

As used herein, the term “powder” means a particulate materialconsisting of a loose aggregation of finely divided solid particles ofwhich the maximum dimension is smaller than 1 millimeter and the averageparticle size is less than 100 microns.

As used herein, the term “film-forming” means that the material forms acontinuous film in the absence of other reagents under the synthesisconditions disclosed herein.

As used herein, the term “non-film-forming” means that the material doesnot form a continuous film in the absence of other reagents under thesynthesis conditions disclosed herein.

As used herein, the term “fabric” means any woven, non-woven, knit,tuft, felt, braid, or bonded material assembled from fibers and/oryarns, including, but not limited to, those used in garments (clothing),sheets, towels, and curtains.

As used herein, the term “fabric care composition” refers to anycomposition that may be applied to a fabric, especially during washingor drying of the fabric, to impart beneficial properties to the fabric.These properties include cleaning, removing oily and greasy marks,making fabrics feel smooth, decrease static cling, impart a pleasingfragrance, reduce drying time, reduce wrinkling and make ironing easier.

The polyurethaneurea compositions provided herein provide surprisinglyimproved shape retention properties to fabrics compared to currentlycommercially available fabric care compositions. Furthermore, they alsoprovide ease of care or easy care properties to fabrics. In other words,fabrics treated with the polyurethaneurea compositions have fewerwrinkles after washing and are easier to iron.

The polyurethaneurea compositions of some embodiments also havesurprisingly good water and oil absorption, especially when applied to afabric. This is particularly important for anti-stain properties. Aftera fabric has been contacted with a polyurethaneurea composition of someembodiments, the polyurethaneurea will absorb moisture and oil fromstain-causing sources and thereby limit the absorption of the fabricitself.

Due to the absorption properties, the polyurethaneurea compositions alsoassist in prolonging fragrance substantiation in a fabric which has beencontacted by the composition. This results from the absorption andsubsequent gradual release of the fragrance by the polyurethaneureacomposition.

There is a range of fragrance materials that deposit well on, or areretained well on, polyurethaneurea compositions. Such materials include,but are not limited to, the following two categories, Category A andCategory B as set forth below.

Category A: hydroxylic materials which are alcohols, phenols orsalicylates, with an octanol/water partition coefficient (P) whosecommon logarithm (log₁₀ P) is 2.5 or greater, and a gas chromatographicKovats index (as determined on polydimethylsiloxane as non-polarstationary phase) of at least 1050.

The octanol-water partition coefficient (or its common-logarithm “logP”)is well-known in the literature as an indicator of hydrophobicity andwater solubility (see Hansch and Leo, Chemical Reviews, 71, 526-616,(1971); Hansch, Quinlan and Lawrence, J. Organic Chemistry, 33, 347-350(1968). Where such values are not available in the literature they maybe measured directly, or estimated approximately using mathematicalalgorithms. Software providing such estimations is availablecommercially, for example “LogP” from Advanced Chemistry Design Inc.

Materials having log₁₀ P of 2.5 or more are somewhat hydrophobic.

Kovats indices are calculated from the retention time in a gaschromatographic measurement referenced to the retention time for alkanes[see Kovats, Helv. Chim. Acta 41, 1915 (1958)]. Indices based on the useof a non-polar stationary phase have been used in the perfumery industryfor some years as a descriptor relating to the molecular size andboiling point of components. A review of Kovats indices in the perfumeindustry is given by T Shibamoto in “Capillary Gas Chromatography inEssential Oil Analysis”, P Sandra and C Bicchi (editors), Huethig(1987), pages 259-274. A common non-polar phase which is suitable is100% dimethyl polysiloxane, as supplied for example under a variety oftrade names such as RP-1 (Hewlett-Packard), CP Sil 5 CB (Chrompack),OV-1 (Ohio Valley) and Rtx-1 (Restek).

Materials of low Kovats index tend to be volatile and are not retainedwell on many fibers.

Category A includes alcohols of general formula ROH where the hydroxylgroup may be primary, secondary or tertiary, and the R group is an alkylor alkenyl group, optionally branched or substituted, cyclic or acyclic,such that ROH has partition coefficient and Kovats properties as definedabove. Alcohols of Kovats index 1050 to 1600 are typicallymonofunctional alkyl or arylalkyl alcohols with molecular weight fallingwithin the range 150 to 230.

Category A also includes phenols of general formula ArOH, where the Argroup denotes a benzene ring which may be substituted with one or morealkyl or alkenyl groups, or with an ester grouping —CO₂A, where A is ahydrocarbon radical, in which case the compound is a salicylate. ArOHhas partition coefficient and Kovats index as defined above. Typically,such phenols with Kovats index 1050 to 1600 are monohydroxylic phenolswith molecular weight falling within the range 150 to 210.

Examples of fragrance materials in category A are1-(2′-tert-butylcyclohexyloxy)-butan-2-ol, 3-methyl-5-(2′,2′,3′-trimethylcyclopent-3-enyl)-pentan-2-ol, 4-methyl-3-decen-5-ol, amylsalicylate, 2-ethyl-4(2′,2′,3-trimethylcyclopent-3′-enyl)but-2-enol,borneol, carvacrol, citronellol, 9-decenol, dihydroeugenol,dihydrolinalol, dihydromyrcenol, dihydroterpineol, eugenol, geraniol,hydroxycitronellal, isoamyl salicylate, isobutyl salicylate, isoeugenol,linalool, menthol, nerolidol, nerol, para tert-butyl cyclohexanol,phenoxanol, terpineol, tetrahydrogeraniol, tetrahydrolinalol,tetrahydromyrcenol, thymol, 2-methoxy-4-methylphenol,(4-isopropylcyclohexyl)-methanol, benzyl salicylate cyclohexylsalicylate, hexyl salicylate, patchouli alcohol, and farnesol.

Category B esters, ethers, nitriles, ketones or aldehydes, with anoctanol/water partition coefficient (P) whose common logarithm (log₁₀ P)is 2.5 or greater, and a gas chromatographic Kovats index (as determinedon polydimethylsiloxane as non-polar stationary phase) of at least 1300.

Fragrances of Category B are of general formula RX, where X may be in aprimary, secondary or tertiary position, and is one of the followinggroups: —CO₂A, —COA, —OA, —CN or —CHO. The groups R and A arehydrocarbon residues, cyclic or non-cyclic and optionally substituted.Typically, the materials of Category B with Kovats index not exceeding1600 are monofunctional compounds with molecular weights in the range160 to 230.

Examples of fragrance materials in category B are1-methyl-4-(4-methyl-3-pentenyl)-3-cyclohexene-1-carbaldehyde,1-(5′,5′-dimethylcyclohexenyl)-pent-en-1-one, 2-heptyl cyclopentanone,2-methyl-3-(4′-tert-butylphenyl)propanal, 2-methylundecanal,2-undecenal, 2,2-dimethyl-3-(4′-ethylphenyl)-propanal,3-(4′-isopropylphenyl)-2-methylpropanal, 4-methyl-4-phenylpent-2-ylacetate, allyl cyclohexyl propionate, allyl cyclohexyloxyacetate, amylbenzoate, methyl ethyl ketone trimers, benzophenone,3-(4′-tert-butylphenyl)-propanal, caryophyllene, cis-jasmone, citraldiethyl acetal, citronellal diethyl acetal, citronellyl acetate,phenylethyl butyl ether, alpha-damascone, beta-damascone,delta-damascone, gamma-decalactone, dihydro isojasmonate,dihydrojasmone, dihydroterpinyl acetate, dimethyl anthranilate, diphenyloxide, diphenylmethane, dodecanal, dodecen-2-al, dodecane nitrile,1-ethoxy-1-phenoxyethane,3-(1′-ethoxyethoxy)-3,7-dimethylocta-1,6-diene,4-(4′-methylpent-3′-enyl)-cyclohex-3-enal, ethyltricyclo[5.2.1.0-2,6-]decane-2-carboxylate,1-(7-isopropyl-5-methylbicyclo[2.2.2]oct-5-en-2-yl)-1-ethanone, allyltricyclodecenyl ether, tricyclodecenyl propanoate, gamma-undecalactone,n-methyl-n-phenyl-2-methylbutanamide, tricyclodecenyl isobutyrate,geranyl acetate, hexyl benzoate, ionone alpha, ionone beta, isobutylcinnamate, isobutyl quinoline, isoeugenyl acetate,2,2,7,7-tetramethyltricycloudecan-5-one, tricyclodecenyl acetate,2-hexylcyclopentanone, 4-acetoxy-3-pentyltetrahydropyran, ethyl2-hexylacetoacetate,8-isopropyl-6-methylbicyclo[2.2.2]oct-5-ene-2-carbaldehyde, methyl4-isopropyl-1-methylbicyclo[2.2.2]oct-5-ene-2-carboxylate, methylcinnamate, alpha iso methyl ionone, methyl naphthyl ketone, nerolin,nonalactone gamma, nopyl acetate, para tert-butyl cyclohexyl acetate,4-isopropyl-1-methyl-2-[1′-propenyl]-benzene, phenoxyethyl isobutyrate,phenylethyl isoamyl ether, phenylethyl isobutyrate, tricyclodecenylpivalate, phenylethyl pivalate, phenylacetaldehyde hexylene glycolacetal, 2,4-dimethyl-4-phenyltetrahydrofuran, rose acetone, terpinylacetate, 4-isopropyl-1-methyl-2-[1′-propenyl]-benzene, yara,(4-isopropylcyclohexadienyl)ethyl formate, amyl cinnamate, amyl cinnamicaldehyde, amyl cinnamic aldehyde dimethyl acetal, cinnamyl cinnamate,1,2,3,5,6,7,8,8a-octathyro-1,2,8,8-tetramethyl-2-acetyl naphthalene,cyclo-1,13-ethylenedioxytridecan-1,13-dione, cyclopentadecanolide, hexylcinnamic aldehyde,1,3,4,6,7,8-hexahydro-4,6,6,7,8,8-hexamethylcyclopenta[g]-2-benzopyran,geranyl phenyl acetate, 6-acetyl-1-isopropyl-2,3,3,5-tetramethylindane,and 1,1,2,4,4,7-hexamethyl-6-acetyl-1,2,3,4-tetrahydronaphthalene.

While this is an extensive list of fragrances and perfumes that workespecially well with spandex compositions, it is recognized that avariety of other fragrances are also useful in some embodiments.Fragrances may include a substance or mixture of substances includingnatural (i.e., obtained by extraction of flowers, herbs, leaves, roots,barks, wood, blossoms or plants), artificial (i.e., a mixture ofdifferent nature oils or oil constituents) and synthetic (i.e.,synthetically produced) odoriferous substances.

A non-limiting list of useful fragrances includes: hexyl cinnamicaldehyde; amyl cinnamic aldehyde; amyl salicylate; hexyl salicylate;terpineol; 3,7-dimethyl-cis-2,6-octadien-1-ol; 2,6-dimethyl-2-octanol;2,6-dimethyl-7-octen-2-ol; 3,7-dimethyl-3-octanol;3,7-dimethyl-trans-2,6-octadien-1-ol; 3,7-dimethyl-6-octen-1-ol;3,7-dimethyl-1-octanol;2-methyl-3-(para-tert-butylphenyl)-propionaldehyde;4-(4-hydroxy-4-methylpentyl)-3-cyclohexene-1-carboxaldehyde;tricyclodecenyl propionate; tricyclodecenyl acetate; anisaldehyde;2-methyl-2-(para-iso-propylphenyl)-propionaldehyde;ethyl-3-methyl-3-phenyl glycidate; 4-(para-hydroxyphenyl)-butan-2-one;1-(2,6,6-trimethyl-2-cyclohexen-1-yl)-2-buten-1-one;para-methoxyacetophenone; para-methoxy-alpha-phenylpropene;methyl-2-n-hexyl-3-oxo-cyclopentane carboxylate; undecalactone gamma,orange oil; lemon oil; grapefruit oil; bergamot oil; clove oil;dodecalactone gamma; methyl-2-(2-pentyl-3-oxo-cyclopentyl) acetate;beta-naphthol methylether; methyl-beta-naphthylketone; coumarin;decylaldehyde; benzaldehyde; 4-tert-butylcyclohexyl acetate;alpha,alpha-dimethylphenethyl acetate; methylphenylcarbinyl acetate;cyclic ethyleneglycol diester of tridecandioic acid;3,7-dimethyl-2,6-octadiene-1-nitrile; ionone gamma methyl; ionone alpha;ionone beta; petitgrain; methyl cedrylone;7-acetyl-1,2,3,4,5,6,7,8-octahydro-1,1,6,7-tetramethyl-naphthalene;ionone methyl; methyl-1,6,10-trimethyl-2,5,9-cyclododecatrien-1-ylketone; 7-acetyl-1,1,3,4,4,6-hexamethyl tetralin;4-acetyl-6-tert-butyl-1,1-dimethyl indane; benzophenone;6-acetyl-1,1,2,3,3,5-hexamethyl indane;5-acetyl-3-isopropyl-1,1,2,6-tetramethyl indane; 1-dodecanal;7-hydroxy-3,7-dimethyl octanal; 10-undecen-1-al; iso-hexenyl cyclohexylcarboxaldehyde; formyl tricyclodecan; cyclopentadecanolide;16-hydroxy-9-hexadecenoic acid lactone;1,3,4,6,7,8-hexahydro-4,6,6,7,8,8-hexamethylcyclopenta-gamma-2-benzopyran-e;ambroxane; dodecahydro-3a,6,6,9a-tetramethylnaphtho-[2,1 b]furan;cedrol; 5-(2,2,3-trimethylcyclopent-3-enyl)-3-methylpentan-2-ol;2-ethyl-4-(2,2,3-trimethyl-3-cyclopenten-1-yl)-2-buten-1-ol;caryophyllene alcohol; cedryl acetate; para-tert-butylcyclohexylacetate; patchouli; olibanum resinoid; labdanum; vetivert; copaibabalsam; fir balsam; hydroxycitronellal and indol; phenyl acetaldehydeand indol; geraniol; geranyl acetate; linalool; linalyl acetate;tetrahydrolinalool; citronellol; citronellyl acetate; dihydromyrcenol;dihydromyrcenyl acetate; tetrahydromyrcenol; terpinyl acetate; nopol;nopyl acetate; 2-phenylethanol; 2-phenylethyl acetate; benzyl alcohol;benzyl acetate; benzyl salicylate; benzyl benzoate; styrallyl acetate;dimethylbenzylcarbinol; trichloromethylphenylcarbinylmethylphenylcarbinyl acetate; isononyl acetate; vetiveryl acetate;vetiverol; 2-methyl-3-(p-tert-butylphenyl)-propanal;2-methyl-3-(p-isopropylphenyl)-propanal;3-(p-tert-butylphenyl)-propanal;4-(4-methyl-3-pentenyl)-3-cyclohexenecarbaldehyde;4-acetoxy-3-pentyltetrahydropyran; methyl dihydrojasmonate;2-n-heptylcyclopentanone; 3-methyl-2-pentyl-cyclopentanone; n-decanal;n-dodecanal; 9-decenol-1; phenoxyethyl isobutyrate; phenylacetaldehydedimethylacetal; phenylacetaldehyde diethylacetal; geranonitrile;citronellonitrile; cedryl acetal; 3-isocamphylcyclohexanol; cedrylmethylether; isolongifolanone; aubepine nitrile; aubepine; heliotropine;eugenol; vanillin; diphenyl oxide; hydroxycitronellal ionones; methylionones; isomethyl ionomes; irones; cis-3-hexenol and esters thereof;indane musk fragrances; tetralin musk fragrances; isochroman muskfragrances; macrocyclic ketones; macrolactone musk fragrances; ethylenebrassylate, and combinations thereof.

The polyurethaneurea compositions of some embodiments may be in the formof an aqueous dispersion or a powder. When a powdered form is desired,it may be isolated from the aqueous dispersion by filtering, drying andgrinding or by spray drying of the dispersion. For either thefilm-forming or non-film-forming dispersions, the solids content of thedispersion may vary. For example, solids content may be from about 5% toabout 50%, including from about 20% to about 40% by weight of thedispersion, and from about 32% to about 37% by weight of the dispersion.

The viscosity of the dispersion may also vary depending on the use.Examples of suitable viscosities include from about 4 cps to about 36cps, including from about 8 cps to about 20 cps. When the dispersion isto be added to a fabric care composition such as a detergent or fabricsoftener, it may be desirable to have a viscosity similar to the fabriccare composition.

The pH of the dispersions may also vary depending on their use. When thefabric care composition to which the dispersion will be added is acidic,the pH of the dispersion should be neutral to acidic and desirably of asimilar pH to the fabric care composition, including pH 7 or less suchas pH 2-4.

To prepare the anionic film-forming aqueous dispersion of someembodiments, a prepolymer is prepared which is a capped glycol. Anexample of a suitable prepolymer is the reaction product of:

at least one hydroxyl-terminated polymer such as a polyether (includingcopolyethers), polycarbonate or polyester polyol component having anumber average molecular weight of about 600 to about 3,500, forexample, a poly(tetramethylene ether) glycol having a number averagemolecular weight of about 1,400 to about 2,400;

a polyisocyanate, which is a mixture of 4,4′- and 2,4′-methylenebis(phenyl isocyanate) (MDI) isomers, with the ratio of the 4,4′-MDI to2,4′-MDI isomers from about 65:35 to about 35:65; and

at least one diol compound with: (i) hydroxy groups capable of reactingwith the mixture of MDI isomers of the polyisocyanate and (ii) at leastone carboxylic acid group capable of forming a salt upon neutralization,wherein the at least one carboxylic acid group is incapable of reactingwith the mixture of MDI isomers of the polyisocyanate.

The prepolymer is then neutralized to form a salt, for example byinclusion of triethylamine and finally chain extended with a diaminechain extender and water to form the aqueous dispersion. Additives suchas surfactants, anti-/de-foamers, antioxidants, thickening agents, andcombinations thereof, may be included.

The MDI isomer mixture useful for the anionic dispersion achieves areduction in the prepolymer viscosity without the addition of a solvent.The MDI isomer mixture also serves to reduce the rate of the reaction.The prepolymer may be prepared either in a batch process or in acontinuous process.

When included in some embodiments, the diol including hydroxy groups anda carboxylic acid group may be described as an acidic diol. Examples ofuseful acidic diols include 2,2-dimethylolacetic acid,2,2-dimethylolpropionic acid (DMPA), 2,2-dimethylolbutanoic acid,2,2-dimethylolpentanoic acid, and combinations thereof.

The nonionic film-forming dispersion of some embodiments includes aprepolymer, which is an isocyanate-terminated polyurethane prepolymer.An example of a suitable prepolymer is the reaction product of ahydroxyl-terminated polymer such as a polyol, such aspoly(tetramethylene-co-ethylene ether) glycol or a mixture ofpoly(tetramethylene ether) glycol with ethoxylated polypropylene glycoland a diisocyanate such as 4,4′-methylenebis(phenyl isocyanate). Thisprepolymer is then chain extended with water and dispersed in water ordispersed in water followed by chain extension with water.

The nonionic non-film-forming dispersion of some embodiments includes aprepolymer, which is an isocyanate-terminated polyurethane prepolymer.This prepolymer is also the reaction product of a polyol such as apolybutadiene glycol or poly(tetramethylene ether) glycol and adiisocyanate such as 4,4′-methylenebis(phenyl isocyanate). Thisprepolymer may be chain extended with a combination of water and adiamine chain extender such as ethylene diamine or an amine-functionalcrosslinker such as polyvinylamine. Either a hydrophilic or hydrophobicglycol may be selected to produce a polymer powder having differentwater/oil absorbing capabilities. Also, the powder particle size can beadjusted by adjusting the viscosity of the prepolymer with the use of asolvent for dilution.

The dispersions of some embodiments may include a prepolymer which is acapped glycol which is dispersed into water for chain extension. For thepreparation of these dispersions, the water may be cooled to allow morecomplete dispersion prior to beginning the chain extension reaction. Forexample the water may be cooled to about 10° C. or less, including about7° C. or less. Water from many sources is useful with the dispersion ofsome embodiments such as distilled water, deionized water or ultra purewater.

The average particle size of the particles in the dispersions may varyfor either the non-film-forming or film-forming-dispersions. Asmentioned above, one factor that affects particle size is the viscosityof the prepolymer. Another factor is the speed of the dispersion, whichfor example may be from about 5000 rpm to about 10,000 rpm including7,000 rpm. Particle size ranges for the dispersions and powders of someembodiments include from about 400 microns (μm) or fewer such as fromabout 0.01 μm to about 0.5 μm, 0.1 μm to about 1.0 μm, about 0.1 μm toabout 5.0 μm, about 0.15 μm to about 0.65 μm, and larger particles suchas from about 10 μm to about 150 μm.

In some embodiments, a polyurethaneurea powder is made by high shearforce dispersion of an isocyanate terminated prepolymer, with or withoutsolvent, into a water medium containing a dispersant, and a chainextension reagent or a cross-linking agent. High shear force is definedas force sufficient to make particles no larger than 500 microns. Theprepolymer can be made by reacting a polyol or a polyol copolymer or apolyol mixture, such as polyether glycols, polyester glycols,polycarbonate glycols, polybutadiene glycols or their hydrogenatedderivatives, and hydroxy-terminated polydimethylsiloxanes, with adiisocyanate such as methylene bis(4-phenylisocyanate) (MDI) to form anNCO-terminated prepolymer or a “capped glycol”. In a polymercomposition, the molar ratio of NCO/OH is in the range of 1.2 to 5.0. Anexample of a chain extension reagent is an aliphatic diamine such asethylene diamine (EDA).

Where cross-linking of the powders is desired, a chain cross-linkingagent may be an organic compound or a polymer with at least threeprimary amine or secondary amine functional groups capable of reactingwith NCO groups.

An organic solvent, soluble or insoluble in water, such as 1-methyl2-pyrrolidinone (NMP) or xylenes can be used to dilute the prepolymerprior to the dispersion. The formed polyurethaneurea polymer fineparticles dispersed in water can be used as such or isolated byfiltration and drying into solid powders. Alternatively, a spray coatingprocess which also provides a greater control of particle size may alsobe used. Another useful method is centrifuge drying.

The particle size of the powders of some embodiments may vary dependingon the desired use. For example, the average particle size may be lessthan 1 millimeter (mm), also including an average particle size of lessthan 100 microns (μm).

In some embodiments, a segmented polyurethaneurea for making anelastomeric powder includes: a) a polyol or a polyol copolymer or apolyol mixture of number average molecular weight between 500 to 5000,including but not limited to polyether glycols, polyester glycols,polycarbonate glycols, polybutadiene glycols or their hydrogenatedderivatives, and hydroxy-terminated polydimethylsiloxanes; b) adiisocyanate including aliphatic diisocyanates, aromatic diisocyanatesand alicyclic diisocyanates; and c) an aliphatic diamine (i.e., adiamine chain extender) or its mixture with at least one diamineselected from the group consisting of an aliphatic diamine and analicyclic diamine, each having 2 to 13 carbon atoms, or anamino-terminated polymer, or an organic compound or a polymer with atleast three primary or secondary amine groups; and optionally amonoamine, primary or secondary, as a chain terminator.

Examples of polyether polyols that can be used in some embodimentsinclude those glycols with two or more hydroxy groups, from ring-openingpolymerization and/or copolymerization of ethylene oxide, propyleneoxide, trimethylene oxide, tetrahydrofuran, and 3-methyltetrahydrofuran,or from condensation polymerization of a polyhydric alcohol, forexample, a diol or diol mixtures, with less than 12 carbon atoms in eachmolecule, such as ethylene glycol, 1,3-propanediol, 1,4-butanediol,1,5-pentanediol 1,6-hexanediol, neopentyl glycol,3-methyl-1,5-pentanediol, 1,7-heptanediol, 1,8-octanediol,1,9-nonanediol, 1,10-decanediol and 1,12-dodecanediol. For example, alinear, bifunctional polyether polyol may be included, specifically, apoly(tetramethylene ether) glycol of molecular weight of about 1,700 toabout 2,100, such as Terathane® 1800 (commercially available fromInvista S.à r.l. of Wichita, Kans. and Wilmington, Del.) with afunctionality of 2. Other examples of useful commercially availablepolyether polyols are marketed as Acclaim® 4220N available from Bayer,Pittsburgh, Pa. and PLURACOL® 1062P available from BASF, Wyandotte,Mich. Other useful polyols include copolymers of tetrahydrofuran andethylene oxide, and copolymers of ethylene oxide and propylene oxide,among others. More than one type of polyol may be combined to providethe polyurethaneurea compositions of some embodiments. For example, whentwo different polyols are used, they may be combined in a ratio fromabout 25:75 to about 75:25 including from about 40:60 to about 60:40 andabout 50:50.

Examples of polyester polyols that can be used include those esterglycols with two or more hydroxy groups, produced by condensationpolymerization of aliphatic polycarboxylic acids and polyols, or theirmixtures, of low molecular weights with no more than 12 carbon atoms ineach molecule. Examples of suitable polycarboxylic acids are malonicacid, succinic acid, glutaric acid, adipic acid, pimelic acid, subericacid, azelaic acid, sebacic acid, undecanedicarboxylic acid anddodecanedicarboxylic acid. Example of suitable polyols for preparing thepolyester polyols are ethylene glycol, 1,3-propanediol, 1,4-butanediol,1,5-pentanediol 1,6-hexanediol, neopentyl glycol,3-methyl-1,5-pentanediol, 1,7-heptanediol, 1,8-octanediol,1,9-nonanediol, 1,10-decanediol and 1,12-dodecanediol. For example, alinear, bifunctional polyester polyol with a melting temperature ofabout 5° C. to about 50° C. may be included.

Examples of polycarbonate polyols that can be used include thosecarbonate glycols with two or more hydroxy groups, produced bycondensation polymerization of phosgene, chloroformic acid ester,dialkyl carbonate or diallyl carbonate and aliphatic polyols, or theirmixtures, of low molecular weights with no more than 12 carbon atoms ineach molecule. Example of suitable polyols for preparing thepolycarbonate polyols are diethylene glycol, 1,3-propanediol,1,4-butanediol, 1,5-pentanediol, 1,6-hexanediol, neopentyl glycol,3-methyl-1,5-pentanediol, 1,7-heptanediol, 1,8-octanediol,1,9-nonanediol, 1,10-decanediol and 1,12-dodecanediol. For example, alinear, bifunctional polycarbonate polyol with a melting temperature ofabout 5° C. to about 50° C. may be included.

Examples of suitable diisocyanate components are 1,6-diisocyanatohexane,1,12-diisocyanatododecane, isophorone diisocyanate,trimethyl-hexamethylenediisocyanates, 1,5-diisocyanato-2-methylpentane,diisocyanato-cyclohexanes, methylene-bis(4-cyclohexyl isocyanate),tetramethyl-xylenediisocyanates, bis(isocyanatomethyl)cyclohexanes,toluenediisocyanates, methylene bis(4-phenyl isocyanate),phenylenediisocyanates, xylenediisocyanates, and a mixture of suchdiisocyanates. For example the diisocyanate may be an aromaticdiisocyanate such phenylenediisocyanate, tolylenediisocyanate (TDI),xylylenediisocyanate, biphenylenediisocyanate, naphthylenediisocyanate,diphenylmethanediisocyanate (MDI) (including 4,4′-methylene bis(phenylisocyante), 2,4′-methylene bis(phenyl isocyante), and combinationsthereof), and combinations of one or more diisocyanates.

Examples of suitable diamine components (diamine chain extenders) areethylenediamine, 1,2-propanediamine, 1,3-propanediamine,2,2-dimethyl-1,3-propanediamine, 1,4-butanediamine, 1,5-pentanediamine,hexamethylene diamine, 1,7-heptanediamine, 1,8-octanediamine,1,9-nonanediamine, 1,10-decanediamine, 1,12-dodecanediamine,2-methyl-1,5-pentanediamine, cyclohexanediamines,cyclohexanebis(methylamine)s, isophorone diamine, xylylenediamines, andmethylenebis(cyclohexylamine)s. A mixture of two or more diamines canalso be used. As mentioned above, water may also be included as a chainextender.

Examples of suitable amine-terminated polymers are bis(3-aminopropyl)terminated polydimethylsiloxane, amine terminatedpoly(acrylonitrile-co-butadiene), bis(3-aminopropyl) terminatedpoly(ethylene glycol), bis(2-aminopropyl) terminated poly(propyleneglycol), and bis(3-aminopropyl) terminated polytetrahydrofuran.

Examples of suitable organic compounds or polymers with at least threeprimary or secondary amine groups are tris-2-aminoethyl amine,poly(amido amine) dendrimers, polyethylenimine, poly(vinylamine), andpoly(allylamine).

Examples of the suitable monoamine component include primary alkylaminessuch as ethylamine, butylamine, hexylamine, cyclohexylamine,ethanolamine and 2-amino-2-methyl-1-propanol, and secondarydialkylamines such as N,N-diethylamine, N-ethyl-N-propylamine,N,N-diisopropylamine, N-tert-butyl-N-methylamine,N-tert-butyl-N-benzylamine, N,N-dicyclohexylamine,N-ethyl-N-isopropylamine, N-tert-butyl-N-isopropylamine,N-isopropyl-N-cyclohexylamine, N-ethyl-N-cyclohexylamine,N,N-diethanolamine, and 2,2,6,6-tetramethylpiperidine.

In making a polyurethaneurea powder of some embodiments, a glycol isfirst reacted with a diisocyanate, optionally with a catalyst present,to form an NCO-terminated prepolymer or a “capped glycol”. This reactionis typically carried out, in a molten form of uniformly blended mixture,with applied heat at temperatures of 45 to 98° C. for a period of 1 hourto 6 hours. The amounts of each reaction component, the weight of theglycol (Wgl) and the weight of the diisocyanate (Wdi), are regulated bythe capping ratio (CR), which is defined as the mole ratio of thediisocyanate to the glycol as shown below:CR=(Wdi/MWdi)/(Wgl/MWgl)

Where MWdi is the molecular weight of the diisocyanate and MWgl is thenumber average molecular weight of the glycol. According to the presentinvention, the capping ratio is in the range of 1.2 to 5.0, specificallybetween 1.5 and 3.0.

After the capping reaction is complete when all of the hydroxy (—OH)groups from the glycol molecules are consumed by the isocyanate (—NCO)groups from the diisocyanate to form a urethane bond, a viscouspolyurethane prepolymer with terminal NCO groups is formed. Thisprepolymer is then added and dispersed into a water solution containingsurface active reagents such as dispersants and anti-/defoamers andoptionally chain-extending agents such as diamines. Alternatively, thisprepolymer can be diluted with an organic solvent such as water-solubleN-methylpyrrolidone (NMP) or water-insoluble xylenes before dispersed inthe water medium. The solid polymer particles are formed under the highshear force during the dispersion and upon the chain extension withwater and/or diamine extenders. These polyurethaneurea particles canthen be filtered and dried.

The polyurethaneurea compositions prepared by the methods describedabove have surprisingly good water and oil absorption, especially whenapplied to a fabric. This is particularly important for anti-stainproperties. After a fabric has been contacted with a polyurethaneureacomposition of some embodiments, the polyurethaneurea will absorbmoisture and oil from stain-causing sources and thereby limit theabsorption of the fabric itself.

Due to the absorption properties, the polyurethaneurea compositions alsoassist in prolonging fragrance substantiation in a fabric which has beencontacted by the composition. This results from the absorption andsubsequent gradual release of the fragrance by the polyurethaneureacomposition.

The fabric care composition of some embodiments may include a fabricsoftener or detergent to which the polyurethaneurea compositions may beadded. These polyurethaneurea compositions may also be in any form suchas a dispersion or powder. Alternatively, the polyurethaneureacomposition may be added directly to the fabric, to a washing machine,wash water (for hand washing), or to an automatic dryer.

Furthermore, the powder or dispersion may be used as a replacement offabric softener to deliver anti stain properties to garments via homelaundering. Fabric softeners are frequently used to deliver perfume orfragrance to fabrics and secondarily to deliver fabric softness. Thefabric softening aspect is not necessarily needed when tumble drying isused since fabrics which are tumble dried are already very soft.

The detergent compositions of some embodiments normally contain ananionic, nonionic, amphoteric or ampholytic surfactant or a mixturethereof, and frequently contains in addition an organic or inorganicbuilder.

Fabric softeners will generally include an active component such as aquaternary ammonium salt. Examples of non-cyclic quaternary ammoniumsalts include tallow trimethyl ammonium chloride; ditallow dimethylammonium chloride; ditallow dimethyl ammonium methyl sulfate;dihexadecyl dimethyl ammonium chloride; di(hydrogenated tallow) dimethylammonium chloride; dioctadecyl dimethyl ammonium chloride; dieicosyldimethyl ammonium chloride; didocosyl dimethyl ammonium chloride;di(hydrogenated tallow) dimethyl ammonium methyl sulfate; dihexadecyldiethyl ammonium chloride; dihexadecyl dimethyl ammonium acetate;ditallow dipropyl ammonium phosphate; ditallow dimethyl ammoniumnitrate; and di(coconut-alkyl) dimethyl ammonium chloride.

Other optional components of the fabric care compositions of someembodiments conventional in nature, and generally are present from about0.01% to about 10% by weight of the composition or dispersion, includingfrom about 0.05 to about 5%, and including from about 2% to about 4%.Such optional components include, but are not limited to, colorants,perfumes, bacterial inhibitors, optical brighteners, opacifiers,viscosity modifiers, fabric conditioning agents in solid form such asclay, fabric absorbency boosters, emulsifiers, stabilizers, shrinkagecontrollers, spotting agents, germicides, fungicides, anti-corrosionagents, etc. Other examples of additives include preservatives such aslactic acid, antioxidants, pigments, colorants, fragrances,anti-microbial agents (like silver), active ingredients (moisturizers,UV-screens), surfactants, anti-/defoamers, solvents and the like can beblended into the polyurethaneurea compositions before, during or afterthe dispersion of the prepolymer. Any active may be used alone or incombination with other additives of similar or dissimilar types. Forexample, suitable surfactants include those available under the brandsBIO-SOFT® and Stepantex® from Stepan Company, Northfield, Ill. andTetranyl available from KAO Corporation. A combination of thesesurfactants may be used in any suitable amount such as a 50/50 blend.

The fabric care compositions of the present invention can be prepared byconventional methods. Homogenizing is not necessary. A convenient andsatisfactory method is to prepare a premix of softeners in water atabout 150° F. which is then added to a hot aqueous solution of the othercomponents. Temperature-sensitive components can be added after thefabric conditioning composition is cooled to about room temperature.

The fabric care compositions of some embodiments may be used by addingto the rinse cycle of conventional home laundry operations.Alternatively, the fabric care compositions may be added to a detergentprior to the wash cycle, directly to the fabric, or with hand washing,either as part of a detergent or fabric softening composition ordirectly to the wash water.

The fabric care compositions may be applied in any form known in the artsuch as a powder, a liquid, a solid tablet, an encapsulate liquid (forexample a composition encapsulated with polyvinylalcohol), or in thecase of application for an automatic dryer, in a non-woven sheet.

The fabric care compositions of some embodiments may be added in anyamount necessary to achieve the desired properties of the fabric. Forexample, the fabric care compositions may be added in an amount fromabout 0.05% to about 1.5%, for example, from about 0.2% to about 1%, byweight of the aqueous rinsing bath or wash water.

When present as an aqueous dispersion, the polyurethaneurea compositionsof some embodiments may be present in the fabric care composition fromabout 0.1% to about 20% by weight of the fabric care composition, forexample from about 5% to about 15% and from about 0.5 to 3%. Whenpresent as a powder, the polyurethaneurea compositions may be present inthe fabric care composition from about 0.1% to about 20% by weight ofthe fabric care composition, for example from about 0.5% to about 10%,or from about 1% to about 5%.

Alternatively, the polyurethaneurea powder or dispersion may be added asa replacement for the fabric care composition instead of as a componentof the fabric care composition, where the polyurethaneurea compositionmay be added as 100%. In this instance, the polyurethaneurea compositionmay be added directly to the wash water or rinsing water in amount fromabout 0.05% to about 1.5%, specifically, from about 0.2% to about 1%, byweight of the rinsing water or wash water.

The features and advantages of the present invention are more fullyshown by the following examples which are provided for purposes ofillustration, and are not to be construed as limiting the invention inany way.

EXAMPLES Example 1

Capped glycol prepolymer, formed from Terathane® E2538 glycol (Suppliedby Invista, S.à r.l.) and Isonate® 125MDR and with a capping ratio of1.696, was obtained from a developmental LYCRA® spandex production line.LYCRA® is Invista's registered trademark for spandex. This prepolymer of300 grams was mixed with 150 grams of NMP solvent in a plastic bottlefor 10 minutes to reduce the viscosity. The diluted mixture was pouredinto a steel tube to be injected into a stainless steel container fordispersing. The container had 2000 grams of de-ionized water, 30 gramsof T DET N14 surfactant (commercially available from Harcros of KansasCity, Kans.) and 4.5 grams of ethylenediamine chain extender which werepremixed and cooled to 5° C. The diluted prepolymer was injected underair pressure at about 40 psi through a tubing of ⅛ inch inner diameter,a high-speed laboratory disperser (model number, HSM-100LC commerciallyavailable from Charles Ross & Son Company of Hauppauge, N.Y.) wasoperated at 5000 rpm. The addition of diluted prepolymer was completedwithin 15 minutes, the formed milky dispersion was continued to dispersefor additional 5 minutes. Back weighing of the container gave the totalamount of diluted capped glycol added into the dispersion being 328grams, equivalent to 218.7 grams of capped glycol prepolymer added intothe dispersion. Additive 65 foam controlling agent of 3 grams(commercially from Dow Corning of Midland, Mich.) was added to thedispersion, and the dispersion was allowed for mixing at 5000 rpm foranother 30 minutes before pouring into a plastic bottle.

The average particle size of the dispersion was determined to be 52.83micron, with 95% of the particles below 202.6 microns, by the use of aMicrotrac X100 particle size analyzer (Leeds, Northrup).

Example 2

The same ingredients and dispersion procedures were used as in Example1, except that 4.5 grams ethylenediamine chain extender was added afterthe diluted prepolymer was dispersed into water mixture. Back weighingof the container gave the total amount of diluted capped glycol addedinto the dispersion being 329 grams, equivalent to 219 grams of cappedglycol prepolymer added into the dispersion. The average particle sizeof the dispersion was determined to be 33.45 micron, with 95% of theparticles below 64.91 microns. The solid polymer particles do not forminto films when isolated.

Example 3

Capped glycol prepolymer was prepared by reacting 500 grams of Krasol®HLB 2000 glycol (Supplied by Sartomer Company, Inc. at Exton, Pa.) and105.86 grams of Isonate® 125MDR at 90° C. for 120 minutes in a 2000 mlreaction kettles equipped with a heating mantle and a mechanicalagitator. The reaction was carried out in a nitrogen filled dry box.After the reaction, the prepolymer had a NCO group wt % of 2.98 asdetermined by titration method. This prepolymer was poured into a steeltube to be injected into a stainless steel container for dispersing.De-ionized water (2000 grams) was mixed at room temperature in thecontainer with 30 grams of T DET N14 surfactant (commercially availablefrom Harcros of Kansas City, Kans.) and 3 grams of Additive 65 foamcontrolling agent (commercially from Dow Corning of Midland, Mich.). Theprepolymer was injected under air pressure at about 80 psi through atubing of ⅛ inch inner diameter, a high-speed laboratory disperser(model number, HSM-100LC commercially available from Charles Ross & SonCompany of Hauppauge, N.Y.) was operated at 5000 rpm. The addition ofdiluted prepolymer was completed within 15 minutes, the formed milkydispersion was continued to disperse for additional 5 minutes. Backweighing of the container gave the total amount of diluted capped glycoladded into the dispersion being 422 grams. Ethylenediamine chainextender of 4.5 grams was added to the dispersion and the dispersion wasallowed for mixing at 5000 rpm for another 30 minutes. The averageparticle size of the formed dispersion was determined to be 49.81micron, with 95% of the particles below 309.7 microns.

Example 4

The procedures were the same as in Example 3, except that a mixture ofglycols with 250 grams of Terathane® 1800 glycol and 250 grams ofKrasol® HLB 2000 glycol was used to form the prepolymer. A total of 465grams of prepolymer was dispersed. The average particle size of theformed dispersion was determined to be 13.67 micron, with 95% of theparticles below 38.26 microns.

Example 5

The preparation of the prepolymers was conducted in a glove box withnitrogen atmosphere. A 2000 ml Pyrex® glass reaction kettle, which wasequipped with an air pressure driven stirrer, a heating mantle, and athermocouple temperature measurement, was charged with about 382.5 gramsof Terathane® 1800 glycol (commercially available from Invista, S.àr.l., Wichita, Kans.) and about 12.5 grams of 2,2-dimethylopropionicacid (DMPA). This mixture was heated to about 50° C. with stirring,followed by the addition of about 105 grams of Lupranate® Mich.diisocyanate (commercially available from BASF, Wyandotte, Mich.). Thereaction mixture was then heated to about 90° C. with continuousstirring and held at about 90° C. for about 120 minutes, after whichtime the reaction was completed, as the % NCO of the mixture declined toa stable value, matching the calculated value (% NCO aim of 1.914) ofthe prepolymer with isocyanate end groups. The viscosity of theprepolymer was determined in accordance with the general method of ASTMD1343-69 using a Model DV-8 Falling Ball Viscometer, (sold by DuratechCorp., Waynesboro, Va.), operated at about 40° C. The total isocyanatemoiety content, in terms of the weight percent of NCO groups, of thecapped glycol prepolymer was measured by the method of S. Siggia,“Quantitative Organic Analysis via Functional Group”, 3rd Edition, Wiley& Sons, New York, pp. 559-561 (1963), the entire disclosure of which isincorporated herein by reference.

Example 6

A solvent-free prepolymer, as prepared according to the procedures andcomposition described in Example 5, was used to make thepolyurethaneurea aqueous dispersion of the present invention.

A 2,000 ml stainless steel beaker was charged with about 700 grams ofde-ionized water, about 15 grams of sodium dodecylbenzenesulfonate(SDBS), and about 10 grams of triethylamine (TEA). This mixture was thencooled with ice/water to about 5° C. and mixed with a high shearlaboratory mixer with rotor/stator mix head (Ross, Model 100LC) at about5,000 rpm for about 30 seconds. The viscous prepolymer, prepared in themanner as Example 1 and contained in a metal tubular cylinder, was addedto the bottom of the mix head in the aqueous solution through flexibletubing with applied air pressure. The temperature of the prepolymer wasmaintained between about 50° C. and about 70° C. The extruded prepolymerstream was dispersed and chain-extended with water under the continuousmixing of about 5,000 rpm. In a period of about 50 minutes, a totalamount of about 540 grams of prepolymer was introduced and dispersed inwater. Immediately after the prepolymer was added and dispersed, thedispersed mixture was charged with about 2 grams of Additive 65(commercially available from Dow Corning®, Midland Mich.). The reactionmixture was then mixed for about another 30 minutes followed by theaddition of about 6 grams of diethylamine (DEA) and additional mixing.The resulting solvent-free aqueous dispersion was milky white andstable.

Example 7

Capped glycol prepolymer, formed from Terathane® 1800 glycol andIsonate® 125MDR (commercially available from the Dow Company, Midland,Mich.) and with a capping ratio of 1.688, was obtained from a commercialLYCRA® spandex production line. LYCRA® is Invista's registered trademarkfor spandex. This prepolymer of 300 grams was mixed with 150 grams ofNMP solvent in a plastic bottle for 10 minutes to reduce the viscosity.The diluted mixture was poured into a steel tube to be injected into astainless steel container for dispersing. The container had 2000 gramsof de-ionized water, 30 grams of T DET N14 surfactant (commerciallyavailable from Harcros of Kansas City, Kans.) and 3 grams ofethylenediamine chain extender which were premixed and cooled to 5° C.The diluted prepolymer was injected under air pressure at about 40 psithrough a tubing of ⅛ inch inner diameter, a high-speed laboratorydisperser (model number, HSM-100LC commercially available from CharlesRoss & Son Company of Hauppauge, N.Y.) was operated at 5000 rpm. Theaddition of diluted prepolymer was completed within 15 minutes, theformed milky dispersion was continued to disperse for additional 5minutes. Back weighing of the container gave the total amount of dilutedcapped glycol added into the dispersion being 347 grams, equivalent to231 grams of capped glycol prepolymer added into the dispersion.Additive 65 foam controlling agent of 3 grams (commercially from DowCorning of Midland, Mich.) was added to the dispersion, and thedispersion was allowed for mixing at 5000 rpm for another 30 minutesbefore pouring into a plastic bottle.

The average particle size of the dispersion was determined to be 32.59micron, with 95% of the particles below 65.98 microns, by the use of aMicrotrac X100 particle size analyzer (Leeds, Northrup). The solidpolymer particles was filtered using a Buchner funnel with Whatman®filter paper under reduced pressure, rinsed the filter cake with waterfor three times, and dried at 60-65° C. for 4 hours. The particles didnot form into films during the filtration or drying. The dried filtercake was easily ground into fine powders with the use of a laboratoryWaring® blender (Blender 700 Model 33BL79 manufactured by Dynamics Inc.,New Hartford, Conn.). In commercial practice, the solid particles wouldbe isolated directly from the dispersion using known drying processessuch as spray drying. The dried powder had a weight average molecularweight of 352,550 and a number average molecular weight of 85,200 asdetermined by GPC.

Example 8

In Example 8 the same components and dispersion procedures were used asin Example 7, except that the solvent used to dilute the capped glycolprepolymer was changed to xylenes, and the amount of ethylenediaminechain extender was increased to 4.5 grams. Back weighing of thecontainer gave the total amount of diluted capped glycol added into thedispersion being 339 grams, equivalent to 226 grams of capped glycolprepolymer added into the dispersion.

The average particle size of the dispersion was determined to be 22.88micron, with 95% of the particles below 46.97 microns. The solid polymerparticles do not form into films when isolated.

Example 9

In Example 9 the same components and dispersion procedures were used asin Example 7, except that the ethylenediamine chain extender wasreplaced by the same amount of a branched polyethylenimine (Mn about 600by GPC from Aldrich). Back weighing of the container gave the totalamount of diluted capped glycol added into the dispersion being 340grams, equivalent to 227 grams of capped glycol prepolymer added intothe dispersion.

The average particle size of the dispersion was determined to be 58.12micron, with 95% of the particles below 258.5 microns. The solid polymerparticles did not form into films when isolated.

Example 10

A glove box with dry nitrogen atmosphere was used to prepare theprepolymer. In two separate 2000 ml Pyrex® glass reaction kettles, whichwas equipped with an air pressure driven stirrer, a heating mantle and athermocouple temperature measurement, each was charged with 220.0 gramsof Terathane® 1800 glycol (commercially available from Invista) and220.0 grams of Pluracol® HP 4000D glycol (commercially available fromBASF). This glycol mixture was heated to 50° C. with stirring, followedby the addition of 75.03 grams of Isonate® 125MDR (commerciallyavailable from Dow Chemical). The reaction mixture was then heated to90° C. with continuous stirring and held at 90° C. for 120 minutes.Samples were taken from the reactor, and determined to have 2.170 and2.169% NCO respectively, as measured by the method of S. Siggia,“Quantitative Organic Analysis via Functional Group”, 3rd Edition, Wiley& Sons, New York, pp. 559-561 (1963).

A 3000 ml stainless steel beaker was charged with 1600 grams ofde-ionized water, 15 grams of T DET N14 surfactant (commerciallyavailable from Harcros of Kansas City, Kans.) and 5 grams of Additive 65(commercially available from Dow Corning). This mixture was then cooledwith ice/water to 10° C. and mixed with a high shear laboratory mixerwith rotor/stator mix head (Ross, Model 100LC) at 5000 rpm for 30seconds. The viscous prepolymers, as prepared above in two reactors,were poured into a metal tubular cylinder and was added to the bottom ofthe mix head in the aqueous solution through a flexible tubing withapplied air pressure. The temperature of the prepolymer was maintainedbetween 50-70° C. The extruded prepolymer stream was dispersed andchain-extended with water under the continuous mixing of 5000 rpm. In aperiod of 5 minutes, a total amount of 616 grams of prepolymer wasintroduced and dispersed in water. After the prepolymer was added anddispersed, the dispersed mixture was mixed for another 40 minutes. Theresulting solvent-free aqueous dispersion was milky white to pale bluecolor, with 28.84 wt % solids content and 44 centipoises viscosity. Thedispersion was cast on a sheet of polyethylene and dried in a fume hoodfor overnight under ambient conditions to form an elastic continuousfilm. By GPC measurement, this film had a weight average molecularweight of 127,900 and a number average molecular weight of 41,000.

Example 11

The procedures and conditions were essentially the same as abovementioned Example 10, except that the surfactant was changed toBio-soft® N1-9 (commercially available from Stepan of Northfield, Ill.).A total of 640 grams of prepolymer, with 2.156 and 2.136% NCO from thetwo reactors, was dispersed into water. The formed solvent-freedispersion had a solids content of 26.12% and viscosity of 51centipoises. The cast and dried elastic film had a weight averagemolecular weight of 133,900 and a number average molecular weight of44,400.

Example 12

A glove box with dry nitrogen atmosphere was used to prepare theprepolymer. In two separate 2000 ml Pyrex® glass reaction kettles, whichwas equipped with an air pressure driven stirrer, a heating mantle and athermocouple temperature measurement, each was charged with 440.0 gramsof Terathane® 1800 glycol (commercially available from Invista) and440.0 grams of Pluracol® 1062 glycol (commercially available from BASF).This glycol mixture was heated to 50° C. with stirring, followed by theaddition of 150.0 grams of Isonate® 125MDR (commercially available fromDow Chemical). The reaction mixture was then heated to 90° C. withcontinuous stirring and held at 90° C. for 120 minutes. Samples weretaken from the reactor, and determined to have approximately 2% NCOrespectively, as measured by the method of S. Siggia, “QuantitativeOrganic Analysis via Functional Group”, 3rd Edition, Wiley & Sons, NewYork, pp. 559-561 (1963).

A 3000 ml stainless steel beaker was charged with 1500 grams of ultrapure water that had been cooled to approximately 10° C., 25.9 grams ofBio-soft® N25-9 and 25.9 grams of Stepantex® VT-90 (both available fromStepan Company) and 10 grams of Additive 65 (commercially available fromDow Corning). This mixture was then mixed with a high shear laboratorymixer with rotor/stator mix head (Ross, Model 100LC) at 7000 rpm for 30seconds. The viscous prepolymers, as prepared above in two reactors,were poured into a metal tubular cylinder and was added to the bottom ofthe mix head in the aqueous solution through a flexible tubing withapplied air pressure. The temperature of the prepolymer was maintainedbetween 50-70° C. The extruded prepolymer stream was dispersed andchain-extended with water under the continuous mixing of 7000 rpm for anadditional 2 minutes. This was followed by the addition of 2.33 grams ofPURAC® lactic acid preservative. The resulting solvent-free aqueousdispersion was milky white to pale blue color, with 35 wt % solidscontent.

Example 13

A glove box with dry nitrogen atmosphere was used to prepare theprepolymer. In two separate 2000 ml Pyrex® glass reaction kettles, whichwas equipped with an air pressure driven stirrer, a heating mantle and athermocouple temperature measurement, each was charged with 440.0 gramsof Terathane® 1800 glycol (commercially available from Invista) and440.0 grams of Pluracol® 1062 glycol (commercially available from BASF).This glycol mixture was heated to 50° C. with stirring, followed by theaddition of 150.0 grams of Isonate® 125MDR (commercially available fromDow Chemical). The reaction mixture was then heated to 90° C. withcontinuous stirring and held at 90° C. for 120 minutes. Samples weretaken from the reactor, and determined to have approximately 2% NCOrespectively, as measured by the method of S. Siggia, “QuantitativeOrganic Analysis via Functional Group”, 3rd Edition, Wiley & Sons, NewYork, pp. 559-561 (1963).

A 3000 ml stainless steel beaker was charged with 1500 grams of ultrapure water that had been cooled to approximately 10° C., 25.9 grams ofBio-soft® N25-9 (available from Stepan Company) and 25.9 grams ofTetranyl® L1/90L available from (KAO Corporation) and 10 grams ofAdditive 65 (commercially available from Dow Corning). This mixture wasthen mixed with a high shear laboratory mixer with rotor/stator mix head(Ross, Model 100LC) at 7000 rpm for 30 seconds. The viscous prepolymers,as prepared above in two reactors, were poured into a metal tubularcylinder and was added to the bottom of the mix head in the aqueoussolution through a flexible tubing with applied air pressure. Thetemperature of the prepolymer was maintained between 50-70° C. Theextruded prepolymer stream was dispersed and chain-extended with waterunder the continuous mixing of 7000 rpm for an additional 2 minutes.This was followed by the addition of 2.33 grams of PURAC® lactic acidpreservative. The resulting solvent-free aqueous dispersion was milkywhite to pale blue color, with 35 wt % solids content.

A glove box with dry nitrogen atmosphere was used to prepare theprepolymer. In two separate 2000 ml Pyrex® glass reaction kettles, whichwas equipped with an air pressure driven stirrer, a heating mantle and athermocouple temperature measurement, each was charged with 440.0 gramsof Terathane® 1800 glycol (commercially available from Invista) and440.0 grams of Acclaim® 4220N (commercially available from Bayer). Thisglycol mixture was heated to 50° C. with stirring, followed by theaddition of 150.0 grams of Isonate® 125MDR (commercially available fromDow Chemical). The reaction mixture was then heated to 90° C. withcontinuous stirring and held at 90° C. for 120 minutes. Samples weretaken from the reactor, and determined to have approximately 2% NCOrespectively, as measured by the method of S. Siggia, “QuantitativeOrganic Analysis via Functional Group”, 3rd Edition, Wiley & Sons, NewYork, pp. 559-561 (1963).

A 3000 ml stainless steel beaker was charged with 1500 grams of ultrapure water that had been cooled to approximately 10° C., 25.9 grams ofBio-soft® N25-9 and 25.9 grams of Stepantex® VT-90 (both available fromStepan Company) and 10 grams of Additive 65 (commercially available fromDow Corning). This mixture was then mixed with a high shear laboratorymixer with rotor/stator mix head (Ross, Model 100LC) at 7000 rpm for 30seconds. The viscous prepolymers, as prepared above in two reactors,were poured into a metal tubular cylinder and was added to the bottom ofthe mix head in the aqueous solution through a flexible tubing withapplied air pressure. The temperature of the prepolymer was maintainedbetween 50-70° C. The extruded prepolymer stream was dispersed andchain-extended with water under the continuous mixing of 7000 rpm for anadditional 2 minutes. This was followed by the addition of 2.33 grams ofPURAC® lactic acid preservative. The resulting solvent-free aqueousdispersion was milky white to pale blue color, with 35 wt % solidscontent.

Example 15 Cotton/LYCRA® Spandex Woven Fabric Testing

Compositions of the present invention were tested in combination withcotton/LYCRA® spandex woven fabric (97% cotton/3% LYCRA® spandex). Thecontrol for this example was fabric washed with non-concentratedConfort™ fabric softener by Unilever. Each of the compositions as shownin Table 1, were used with the cotton/LYCRA® spandex woven fabric bywashing with Ariel™ liquid detergent on program 4 at 40° C. on aSchutless® programmable automatic washing machine using standard loadfabric to reach 2.5 kg and rinsing with 30 ml of the fabric softenercomposition. After tumble drying (at moderate temperature), the fabricswere evaluated for any deposit on the surface. Neither of the fabricsshowed any deposition of powder or film.

The compositions in Table 1 are as follows:

-   -   Fabric softener (control)    -   Fabric softener, 1% wt of the dispersion of example 6, a film        forming anionic polyurethaneurea water, and 2% wt of Unimer        (synthetic wax to improved dispersion)    -   Fabric softener, 1% wt of the polyurethaneurea powder of example        5, and 2% wt of Unimer (synthetic wax to improved dispersion).

Mixing of the compositions (b) and (c) including the fabric softenerdelivered a homogeneous dispersion (no sedimentation nor agglomeration).

Each fabric was evaluated for easy care. Standard test method AATCC TM124/ISO 15487 was used to determine the durable press rating (“Drating”)before and after ironing. “DP rating” is a measure of thethree-dimensional smoothness of the fabric. Iron gliding or ease ofironing was measured as the time for the iron to glide over a givenlength of fabric with the ironing board at an angle of approximately20°. The easy care results are shown in Table 1. TABLE 1 Easy Care DPRating DP rating after ease of ironing Fabric before ironing ironing (s)(a) 1 1.5 5 (b) 1.5 2.5 3.5 (c) 1.5 2.5 3

From the results in Table 1, it is shown that both fabrics treated withpowder or dispersion show a better improvement of DP rating (1 pointgained after ironing) as compared to the control (0.5 point gained afterironing).

Also the fabrics (b) and (c) treated with the compositions of thepresent invention show a faster gliding of the iron on the fabricsurface.

The compositions (a), (b), and (c) were also evaluated forperfume/fragrance substantiation. Three people were allowed separatelysmell each of the fabrics. Each of these people observed a strongerfragrance in the treated fabrics (b) and (c) which were treated with thecompositions of the present invention.

Absorption properties (moisture management) of fabrics including thosetreated with the compositions of the present invention have also beentested. These properties were measured to demonstrate the differences offabrics after treatment with the powders or dispersions of the presentinvention as compared to untreated fabrics.

For each of the fabrics (a), (b), and (c) as described above, one drop(approximately 30 micro liters) each of linseed oil and water wasapplied to the surface of the fabric. The time until complete absorptionof each droplet was measured and reported in seconds (s) in Table 2. Thearea of the drop surface at 60 seconds following complete absorption bythe fabric was also measured and reported as square centimeters (cm²) intable 2. TABLE 2 Moisture Management absorption time (s) planar wicking(cm²) water oil water oil (a) 138 434 7.28 7.56 (b) 105 382 4.64 6.75(c) 81 320 4.50 6.41

As shown in Table 2, the dispersion (b) and powder (c) of the presentinvention offered improvement in comparison to the control (a) withrespect to absorption. The use of the powder form (c) showed significantimprovement.

Example 16 100% Cotton Woven Fabric Testing

A 100% cotton woven fabric was also tested after treatment with acomposition of the present invention. The control for this example was aconcentrated fabric softener, Softlan™ Ultra by Colgate Palmolive. Eachof the compositions as shown in Table 3, were used with 100% cottonfabric by washing with Ariel™ liquid detergent on program 4 at 40° C. ona Schutless® programmable automatic washing machine using standard loadfabric to reach 2.5 kg load and rinsing with 30 ml of the fabricsoftener composition. After tumble drying (at moderate temperature), thefabrics were evaluated for any deposit on the surface. Neither of thefabrics showed any deposition of power or film.

The compositions in Table 3 are as follows:

-   -   (e) Fabric softener (control)    -   (f) Fabric softener and 10% wt of the dispersion of example 10,        a non-ionic polyurethaneurea dispersion

Mixing of the composition (f) including the fabric softener delivered ahomogeneous dispersion (no sedimentation nor agglomeration).

In order to test the fabrics for growth, first the available stretch ormaximum stretch was calculated. The available stretch was determined byfirst conditioning a fabric specimen followed by cycling three times ona constant-rate-of-extension tensile tester between 0-30N. The maximumstretch was calculated by the following formula:Maximum stretch %=(ML×GL)×100/GL

-   -   Where:    -   ML is the length in mm at 30N; and    -   GL is the gauge length of 250 mm

Separate specimens of each fabric were then extended to 80% of the“available stretch” and held for about 30 min. The fabric specimens werethen allowed to relax for about 60 minutes and growth was measured andcalculated according to:Growth %=L2/L*100

-   -   Where:    -   growth is recorded as a percent after relaxation;    -   L2=the increased length in cm after relaxation; and    -   L=the original length in cm

Each of the fabrics (e) and (f) were measured for fabric elongation. Theresults are shown in Table 3 TABLE 3 Fabric Growth (weft direction)fabric growth (%) (e) 7.4 (f) 5.8

Fabric growth is a measure of shape retention or shape recovery. Growthvalues represent the un-recovered elongation during wear. A lower valuein growth demonstrates that the fabric has a better ability to recoverits initial shape.

Fabrics (e) and (f) were also tested for difference in release ofperfume after a washing and rinsing cycle. One to two grams of eachfabric sample was placed in a sealed gas sampling vessel. Fabricstressing was conducted by shaking with steel ball bearings. Thevolatile compounds released from the sample were drawn out of theheadspace of the gas sampling vessel through a Tenex™ sampling tubeusing a gas sampling pump operating at 50 cc per minute for 20 minutes.The Tenex™ tube trapped the volatile organic compounds (VOC) foranalysis. The Tenex™ tube was then thermally desorbed with the volatileorganics directed into a GC/MS for analysis. The results of the VOCmeasures in Table 3a show that more perfume released from the fabricrinsed with the fabric softener which contains the dispersion of example10, a non-ionic polyurethaneurea dispersion TABLE 3a VOC testingVolatile concentration Fabric ng/L/g (e) 7 (f) 48

Example 17 Spandex/Cotton Blend Fabric Testing

A spandex/cotton blend woven fabric was also tested after treatment witha composition of the some embodiments. The control for this example wasa concentrated fabric softener, Softlan™ Ultra by Colgate Palmolive.Each of the compositions as shown in Table 4, were used withcotton/spandex blend fabric by washing with Ariel™ liquid detergent onprogram 4 at 40° C. on a Schutless® programmable automatic washingmachine using standard load fabric to reach 2.5 kg load and rinsing with18 g of the fabric softener composition. After tumble drying (atmoderate temperature), the fabrics were evaluated for any deposit on thesurface. Neither of the fabrics showed any deposition of powder or film.

The compositions in Table 4 are as follows:

-   -   (g) Fabric treated with fabric softener only (control)    -   (h) Fabric treated with fabric softener and 10% wt of the        dispersion of example 10, a non-ionic polyurethaneurea        dispersion

Mixing of the composition (h) including the fabric softener delivered ahomogeneous dispersion (no sedimentation, nor agglomeration). Each ofthe fabrics (g) and (h) were measured for fabric growth. The results areshown in Table 4: TABLE 4 Fabric Growth (weft direction) fabric growth(%) (g) 4.8 (h) 3.8

Fabric growth is a measure of shape retention. Growth values representthe un-recovered elongation during wear. A lower value in growthdemonstrates that the fabric has a better ability to recover its initialshape

Two LYCRA® spandex/cotton blend fabrics were also tested after treatmentwith a composition of some embodiments. The control for this example wasa concentrated fabric softener, Soupline™ Ultra by Colgate Palmolive.Each of the compositions as shown in Tables 4a and 4b, were used withcotton and LYCRA® spandex blend fabric by washing with Dixan® geldetergent available from Henkel Corporation at 40° C. with standardprogram on a Miele™ commercial washing, using standard load fabric toreach 2.5 kg load and rinsing with 30 ml of fabric softener composition.After tumble drying (at moderate temperature), the fabrics wereevaluated for any deposit on the surface. Neither of the fabrics showedany deposition of powder or film. For the fabrics below, CK is acircular knitted fabric with 95% cotton-5% LYCRA® spandex and WOV is agray weft stretch woven fabric, with 97% cotton-3% LYCRA® spandex.

The compositions in Table 4a and 4b are as follows:

(i)) fabric treated with fabric softener only (control-CK)

(k)) fabric treated with fabric softener and 10% wt (3% activeingredient) of the dispersion of example 10, a non-ionicpolyurethaneurea dispersion (treated-CK)

(k) fabric treated with fabric softener only (control-WOV)

(I) fabric treated with fabric softener and 10% wt (3% activeingredient) of the dispersion of example 10, a non-ionicpolyurethaneurea dispersion (treated-WOV) TABLE 4a Fabric growth CKfabric Growth % (i) length direction 7.5 (j) length direction 7.2 (i)width direction 6.9 (j) width direction 6.4

TABLE 4b Fabric growth WOV fabric Growth % (k) weft direction 7.29 (l)weft direction 6.97

Example 18 Cotton Knit Fabric Testing

A 100% cotton circular knit fabric was also tested after treatment witha composition of the some embodiments. The control for this example waswashed with a concentrated fabric softener, Softlan™ Ultra by ColgatePalmolive. Each of the compositions as shown in Table 5, were used withcotton fabric by washing with Ariel™ liquid detergent on program 4 at40° C. on a Schutless® programmable automatic washing machine usingstandard load fabric to reach 2.5 kg load and rinsing with 30 ml of thefabric softener composition. After tumble drying (at moderatetemperature), the fabrics were evaluated for any deposit on the surface.Neither of the fabrics showed any deposition of powder or film.

The compositions in Table 5 are as follows:

-   -   (m) Fabric treated with fabric softener only (control)    -   (n) Fabric treated with fabric softener and 10% wt of the        dispersion of example 12 (3% wt solids), where the combination        of the dispersion and fabric softener provides a cationic        polyurethaneurea dispersion

Mixing of the composition used in (n) including the fabric softenerprovided a homogeneous dispersion (no sedimentation, nor agglomeration).Each of the fabrics (m) and (n) were measured for fabric growth, using atesting method, as described below.

Growth & Recovery Test Method for Circular Knitted Fabrics DEFINITIONS

“Growth %”—the un-recovered length of a specimen which has been held ata specified elongation (in our case a cycling elongation) for a specificinterval of time then allowed to relax for another specific interval oftime. Growth is expressed as a percentage of the original length.

“Recovery Power”—the remaining force for specific elongations of aspecimen which has been held at a specified elongation (in our case acycling elongation).

According to the method, fabric specimens, such as circular knit (CK)fabrics, are extended following a programmed cycle described below. Atthe end of the cycles, “Recovery Power” is measured at differentelongations. Specimens are then allowed to relax. “Growth” is measuredand calculated after different times of relaxation.

Fabric Specimens were prepared by cutting 7 rectangular of approximately38 cm×5 cm. The specimens were taken at least 10 cm from the selvedgeselecting specimens as far apart as possible in each fabric piece and insuch a way that none contains the same yarns. The fabric specimens werethen conditioned for at least 16 hours at 20° C.±2° C. and 65%±2% R.H.The specimens were laid on a flat surface and a mark places on eachfabric in the middle, 2 lines 28 cm apart.

An “INSTRON” dynamometer, table model No. 5500R was turned on waiting atleast 15 minutes to stabilize the load cell. The specimen clamps weremounted and fixed at the 30 cm position. The fabric specimen was mountedon the claims without tension on the fabric. The fabric specimen wasextended from 0 to 30% of extension (rate: 900 mm/min) then held at thisextension for 1 minute. The specimen was then extended from 30% to 45%of extension 4 times. At the end of the 5^(th) cycle, the clamps reachtheir original position (30 cm). During this last step, force wasmeasured for 45%, 40%, 35%, 30%, 25% and 20% elongation (this is therecovery power).

The fabric specimen was immediately removed from the clamps and allowedto relax on a flat surface. At 1 min, the length between the lines onthe fabric was recorded. This measurement was repeated at 10, 20, 30, 60minutes and 22 hours. The procedure was repeated for each of theremaining fabric specimens

Growth was then calculated as:Growth (%)=(L2−L)/L×100

-   -   where:    -   “Growth” in % after relaxation    -   L2=length in cm between the marked lines after relaxation    -   L=original length in cm (28 cm)

“Recovery Power” was directly determined on the unload curveForce=f(elongation) at 45%, 40%, 35%, 30%, 25% and 20% of elongation

The results after 60 min and 22 hours relaxation are shown in Table 5:TABLE 5 Fabric Growth after 60 minutes (width direction) Growth after 60min Growth after 22 hours fabric (%) (%) (m) 6.5561 6.1735 (n) 5.25515.0000

Fabric growth is a measure of shape retention. Growth values representthe un-recovered elongation during wear. A lower value in growthdemonstrates that the fabric has a better ability to recover its initialshape

While there have been described what are presently believed to be thepreferred embodiments of the invention, those skilled in the art willrealize that changes and modifications may be made thereto withoutdeparting from the spirit of the invention, and it is intended toinclude all such changes and modifications as fall within the true scopeof the invention.

1. A fabric care composition comprising: (a) a detergent or fabricsoftener composition; and (b) a polyurethaneurea in the form of a powderor an aqueous dispersion.
 2. The composition of claim 1, wherein saiddetergent or fabric softener is compatible for use in a washing machine.3. The composition of claim 1, wherein said detergent or fabric softeneris compatible for hand washing.
 4. The composition of claim 1, whereinsaid detergent or fabric softener is in a form selected from the groupconsisting of a powder, a liquid, a solid tablet, an encapsulatedliquid, and a non-woven sheet.
 5. The composition of claim 1, whereinsaid polyurethaneurea comprises a reaction product of anisocyanate-terminated polyurethane prepolymer and a chain extender. 6.The composition of claim 5, wherein said chain extender is selected fromthe group consisting of a diamine chain extender, water, andcombinations thereof.
 7. The composition of claim 1, wherein saidpolyurethaneurea is in the form of a powder and said prepolymer is areaction product of: a hydroxyl-terminated polymer selected from thegroup consisting of a polyether, a polycarbonate, a polyester, andcombinations thereof; and a diisocyanate.
 8. The composition of claim 1,wherein said polyurethaneurea is in the form of an aqueous dispersionand said prepolymer is a reaction product of: a hydroxyl-terminatedpolymer selected from the group consisting of a polyether, apolycarbonate, a polyester, and combinations thereof; a diisocyanate;and optionally an acidic diol.
 9. The composition of claim 8, whereinsaid aqueous dispersion is selected from the group consisting of ananionic dispersion and a non-ionic dispersion.
 10. The composition ofclaim 8, wherein said hydroxyl-terminated polymer is a polyether polyol,said diisocyante is an aromatic diisocyanate selected from the groupconsisting of phenylenediisocyanate, tolylenediisocyanate (TDI),xylylenediisocyanate, biphenylenediisocyanate, naphthylenediisocyanate,diphenylmethanediisocyanate (MDI), and combinations thereof, and saidacidic diol is selected from the group consisting of2,2-dimethylolacetic acid, 2,2-dimethylolpropionic acid,2,2-dimethylolbutanoic acid, 2,2-dimethylolpentanoic acid, andcombinations thereof.
 11. The composition of claim 8, wherein saidpolymer is poly(tetramethylene ether) glycol, said diisocyante is4,4′-methylene bis(phenyl isocyante) or a mixture of 4,4′-methylenebis(phenyl isocyante) and 2,4′-methylene bis(phenyl isocyante), and saidacid glycol is 2,2-dimethylolpropionic acid or is absent.
 12. Acomposition comprising a nonionic film-forming dispersion, wherein saiddispersion comprises water and a polymer; said polymer comprises areaction product of a prepolymer and water as a chain extender; and saidprepolymer consisting essentially of a reaction product of a glycol or amixture of glycols and 4,4′-methylenebis(phenyl isocyanate).
 13. Thecomposition of claim 12, wherein said glycol is selected from the groupconsisting of poly(tetramethylene-co-ethylene ether) glycol and amixture of poly(tetramethylene ether) glycol with ethoxylatedpolypropylene glycol.
 14. The composition of claim 12 further comprisingadditives selected from the group consisting of surfactants, defoamers,pigments, solvents, and combinations thereof.
 15. A compositioncomprising a nonionic non-film-forming dispersion, wherein saiddispersion comprises water and a polymer; said polymer comprises areaction product of a prepolymer and a chain extender comprising adiamine chain extender and water; and said prepolymer consistingessentially of a reaction product of a glycol and4,4′-methylenebis(phenyl isocyanate).
 16. The composition of claim 15further comprising additives selected from the group consisting ofsurfactants, defoamers, pigments, solvents, and combinations thereof.17. A polyurethaneurea powder derived from a composition comprising anonionic non-film-forming dispersion, wherein said dispersion compriseswater and a polymer; said polymer comprises a reaction product of aprepolymer and a chain extender comprising a diamine chain extender andwater; and said prepolymer consisting essentially of a reaction productof a glycol and 4,4′-methylenebis(phenyl isocyanate).
 18. A method ofextending perfume substantiation on a fabric comprising contacting saidfabric with a composition comprising a fragrance and a polyurethaneureain the form of a powder or an aqueous dispersion.
 19. The method ofclaim 18, wherein said fabric comprises a garment.
 20. A method ofincreasing garment shape retention comprising contacting a garment witha polyurethaneurea in the form of a powder or an aqueous dispersion. 21.A method of enhancing ease of care properties of a fabric comprisingcontacting said fabric with a polyurethaneurea in the form of a powderor an aqueous dispersion.
 22. The method of claim 21, wherein saidfabric comprises a garment.
 23. A method of imparting anti-stainproperties to a fabric comprising contacting said fabric with apolyurethaneurea in the form of a powder or an aqueous dispersion. 24.The method of claim 23, wherein said fabric comprises a garment.